Structural and tribological properties of nanostructured supersonic cold sprayed $Ni20 wt.% Sn$ coatings / E. P. Georgiou, S. Dosta, J. Fernández, P. Matteazzi, K. KOWALSKI, J. KUSIŃSKI, R. R. Piticescu, J.-P. Celis // Journal of Thermal Spray Technology ; ISSN 1059-9630. — 2016 — vol. 25 iss. 5, s. 1029–1039. — Bibliogr. s. 1038–1039. — Publikacja dostępna online od: 2016-05-12
Autorzy (8)
- Georgiou E. P.
- Dosta S.
- Fernández J.
- Matteazzi P.
- AGHKowalski Kazimierz
- AGHKusiński Jan
- Piticescu R. R.
- Celis J.-P.
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 99334 |
|---|---|
| Data dodania do BaDAP | 2016-08-26 |
| Tekst źródłowy | URL |
| DOI | 10.1007/s11666-016-0418-4 |
| Rok publikacji | 2016 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | Journal of Thermal Spray Technology |
Abstract
80-μm-thick nanostructured coatings consisting of a Ni solid solution, Ni3Sn, Ni3Sn2, and metastable NiSn intermetallic phases were deposited via supersonic cold spraying onto inconel 718 alloy substrates. These coatings have complex nanostructured metallurgical phases as revealed by transition electron microscopy, scanning electron microscopy, and x-ray diffraction techniques. Their mechanical properties were determined by nanoindentation measurements. Furthermore, the wear behavior of these nanostructured sprayed coatings was compared to the one of the industrial bulk or sprayed coated benchmark materials. It was found that the nanostructured coatings exhibit higher wear resistance than the industrial benchmarks, thanks to an appropriate balance of hard intermetallic phases and soft Ni matrix, as well as to their nanostructuring. Their frictional characteristics under reciprocating sliding are mainly determined by the formation of an oxide-based tribo-layer, which was analyzed by x-ray photoelectron spectroscopy. The role of intermetallic phases in these coatings on the friction and wear is also discussed.