Iron diffusivity into superconducting $YBa_2Cu_3O_{7−\delta}$ at oxygen-assisted sintering: structural, magnetic, and transport properties / Paweł Pęczkowski, Piotr Zachariasz, Marcin KOWALIK, Waldemar TOKARZ, Sugali Pavan Kumar Naik, Jan ŻUKROWSKI, Cezariusz Jastrzębski, Longji Joseph Dadiel, Wojciech TABIŚ, Łukasz GONDEK // Journal of the European Ceramic Society ; ISSN 0955-2219. — Tytuł poprz.: International Journal of High Technology Ceramics. — 2021 — vol. 41 iss. 14, s. 7085–7097. — Bibliogr. s. 7096–7097, Abstr. — Publikacja dostępna online od: 2021-06-15. — M. Kowalik – dod. afiliacja: Rzeszów University of Technology ; W. Tabiś - dod. afiliacja: Institute of Solid State Physics, TU Wien, Austria
Autorzy (10)
- Pęczkowski Paweł
- Zachariasz Piotr
- AGHKowalik Marcin
- AGHTokarz Waldemar
- Naik Sugali Pavan Kumar
- AGHŻukrowski Jan
- Jastrzębski Cezariusz
- Dadiel Longji Joseph
- AGHTabiś Wojciech
- AGHGondek Łukasz
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 136584 |
|---|---|
| Data dodania do BaDAP | 2021-09-30 |
| Tekst źródłowy | URL |
| DOI | 10.1016/j.jeurceramsoc.2021.06.018 |
| Rok publikacji | 2021 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | Journal of the European Ceramic Society |
Abstract
Optimization of materials exhibiting high-temperature superconductivity for producing controllable nano-devices is crucial for industrial applications. Herein we report a comprehensive study of the diffusion process between YBa2Cu3O7−δ (YBCO) and iron particles. Fe diffusion into the YBCO matrix could be fundamental for multilayer systems with YBCO/Fe-alloy interfaces. We have found that the orthorhombic YBCO structure adopts to 3 wt% Fe, while for higher Fe content, a formation of BaFeO3−δ and iron oxides was observed. Complementary measurements confirmed the strong superconductivity suppression in YBCO-Fe materials containing more than 7 wt% Fe. The YBCO with diffused Fe material retain the unit cell orthorhombicity (max. 3 wt% Fe), and their superconducting properties follow the principle of critical scaling with different exponents (γ). The critical current density (Jc), pinning fields (HP) exhibit γ = 1, the first critical field (Hc1) shows γ = 1/2, and critical temperature (Tc) demonstrates γ = 7/4.