$LiNi_{0.6}Co_{0.4-z}Ti_zO_2$ - New cathode materials for Li-ion batteries / Dominika BASTER, Piotr Paziak, Magdalena ZIĄBKA, Gabriela Ważny, Janina MOLENDA // Solid State Ionics ; ISSN 0167-2738. — 2018 — vol. 320, s. 118–125. — Bibliogr. s. 125, Abstr. — Publikacja dostępna online od: 2018-03-06. — SSI-21 : 21st International Conference on Solid State Ionics : Padua, Italy, 18–23 June 2017
Autorzy (5)
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 113565 |
|---|---|
| Data dodania do BaDAP | 2018-05-10 |
| Tekst źródłowy | URL |
| DOI | 10.1016/j.ssi.2018.03.002 |
| Rok publikacji | 2018 |
| Typ publikacji | referat w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | Solid State Ionics |
Abstract
In this work series of LiNi0.6Co0.4−zTizO2 (z = 0.1, 0.2, 0.3) new cathode materials for lithium-ion batteries were studied in terms of their structural, transport and electrochemical properties in Li/Li+/LixNi0.6Co0.4−zTizO2 cells. The materials were synthesized by a high temperature solid-state reaction. XRD measurements with Rietveld analysis confirmed presence of a single phase with hexagonal crystal system with R-3 m space group for LiNi0.6Co0.3Ti0.1O2, and LiNi0.6Co0.2Ti0.2O2. Except for composition LiNi0.6Co0.1Ti0.3O2, which was refined by Rietveld method as cubic-close-packed structure. Electrical conductivity shows thermally activated character for all obtained cathode materials with very low activation energy in range from 0.001 eV to 0.062 eV. The highest values of electrical conductivity were recorded for LiNi0.6Co0.1Ti0.3O2 oxide. With increasing titanium content in LiNi0.6Co0.4−zTizO2 (z = 0.1, 0.2, 0.3) the increase of electrical conductivity was observed. Electrochemical studies performed for Li/Li+/LixNi0.6Co0.4−zTizO2 cell revealed enhancement of electrochemical performance after replacement of Co ions with 0.1 mol of Ti ions. The highest discharge capacity equal to 100 mAh/g at C/20 discharge rate, together with high stable voltage around ~4.2 V was achieved for LiNi0.6Co0.3Ti0.1O2 composition. Among considered cathode materials, LiNi0.6Co0.3Ti0.1O2 is the most promising for further development.