Modeling of the Mn and S microsegregation during continuous casting of rail steel / S. GERASIN, D. KALISZ // Archives of Foundry Engineering / Polish Academy of Sciences. Commission of Foundry Engineering ; ISSN 1897-3310. — Tytuł poprz.: Archiwum Odlewnictwa. — 2015 — vol. 15 spec. iss. 4, s. 35–38. — Bibliogr. s. 38, Abstr., Streszcz.
Autorzy (2)
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 95995 |
|---|---|
| Data dodania do BaDAP | 2016-02-12 |
| Rok publikacji | 2015 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | Archives of Foundry Engineering |
Abstract
The aim of this study was to analyze the process of manganese sulfide formation based on thermodynamics calculation. Both experimental and theoretical analysis methods were used in this work. Computer simulation with the use of non-commercial software was used for the calculation of the process of segregation of manganese and sulfur and MnS non-metallic particles precipitates in liquid steel during solidification of ingot. The curves illustrating the inclusion formation process are presented. MnS inclusions are disposed along grain boundaries in thin layers and have a rounded shape.
Streszczenie
W pracy analizowano proces powstawania siarczku manganu w oparciu o obliczenia termodynamiczne. Wyniki przedstawiono w odniesieniu do badań eksperymentalnych. Symulacje komputerowe procesu segregacji manganu i siarki oraz powstawania wydzieleń MnS podczas krzepnięcia stali zostały wykonane za pomocą nie komercyjnego programu komputerowego. Rezultaty symulacji komputerowej przedstawiono w postaci wykresów prezentujących segregację składników oraz krzywych obrazujących proces powstawania wydzieleń. Wtrącenia MnS są rozmieszczone wzdłuż granic ziaren i mają zaokrąglony kształt.