The kinetics of phase transformations of undercooled austenite of the $38MnCrNi6-4-4$ hypoeutectoid steel / E. ROŻNIATA, R. DZIURKA, R. DĄBROWSKI // Journal of Achievements in Materials and Manufacturing Engineering ; ISSN 1734-8412. — 2012 — vol. 55 iss. 2, s. 280–284. — Bibliogr. s. 284, Abstr.
Autorzy (3)
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 72142 |
|---|---|
| Data dodania do BaDAP | 2013-03-04 |
| Tekst źródłowy | URL |
| Rok publikacji | 2012 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Creative Commons | |
| Czasopismo/seria | Journal of Achievements in Materials and Manufacturing Engineering |
Abstract
Purpose: Present work corresponds to the research on the kinetic of phase transformation of undercooled austenite of 38MnCrNi6-4-4 hypoeutctoid steel. The kinetic of phase transformation of under cooled austenite of investigated alloy was presented on CCT diagram (continuous cooling transformation). Also the methodology of a dilatometric samples preparation and the method of the critical points determination were described. Design/methodology/approach: The austenitising temperature was defined in a standard way i.e. 30-50°C higher than Ac3 temperature for hypoeutectoid steels. The technology of full annealing was proposed for the iron based alloy. The CCT diagram was made on the grounds of dilatograms recorded for samples cooled with various rates. The microstructure of each dilatometric sample was photographed after its cooling to the room temperature and the sample hardness was measured. Findings: The test material has been hypoeutectoid steel. These steels represent a groups of alloy steels for quenching and tempering. The microstructure of test 38MnCrNi6-4-4 hypoeutectoid steel on CCT diagram changes depending on the cooling rate. Practical implications: The paper contains a description of one from a group of iron based model alloys with 0.35-0.40% carbon content. According to PN-EN 10027 standard this steel should have a symbol 38MnCrNi6-4-4. Originality/value: The new hypoeutectoid steel (Mn-Cr-Ni iron based model alloy).