Identification of rheological parameters on the basis of various types of compression and tension tests / Jerzy GAWĄD, Roman Kuziak, Łukasz MADEJ, Danuta SZELIGA, Maciej PIETRZYK // Steel Research International ; ISSN 1611-3683. — Tytuł poprz.: Steel Research. — 2005 — vol. 76 no. 2/3, s. 131–137. — Bibliogr. s. 137
Autorzy (5)
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 20280 |
|---|---|
| Data dodania do BaDAP | 2005-03-05 |
| Tekst źródłowy | URL |
| DOI | 10.1002/srin.200505984 |
| Rok publikacji | 2005 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | Steel Research International |
Abstract
The objective of the project was to determine flow stress on the basis of various plastometric tests. The experiments used uniaxial compression, ring compression, and plane strain compression for two sizes of samples and tensile tests. The material was carbon-manganese steel, and all the tests were performed at three temperatures (900, 1000, and 1100degreesC) and at three strain rates for each temperature (0.1, 1, and 10 s(-1)). Inverse analysis was applied to the interpretation of the results of all compression tests. The flow stresses obtained from various compression tests were compared resulting in the following observations: consistent results between the tests were observed for low values of the Zener-Hollomon parameter, but some discrepancies appeared for larger values of this parameter. The sensitivity of the results of inverse analysis with respect to the friction factor was investigated next, and it was concluded that the flow stress determined from ring compression showed the largest sensitivity to friction. This sensitivity was lower for uniaxial compression and plane strain compression of small samples, and no sensitivity was observed for plane strain compression of large samples. Finally, the simulations of the tensile tests were performed using the rheological models determined in compression, and reasonably good results were obtained.