Magneto-structural properties of multielement $Ni–Cu–Co–Mn–Sn$ Heusler bulk alloys / Anna Wójcik, Wojciech Maziarz, Maciej Szczerba, Marcin SIKORA, Antoni ŻYWCZAK, Lukasz Hawelek, Eduard Cesari // Physica Status Solidi. A, Applications and Materials Science ; ISSN 1862-6300. — Tytuł poprz.: Physica Status Solidi. A, Applied Research ; ISSN: 0031-8965. — 2018 — vol. 215 iss. 23 art. no. 1800358, s. 1800358-1–1800358-6. — Bibliogr. s. 1800358-5–1800358-6. — Publikacja dostępna online od: 2018-08-26. — A. Wójcik – afiliacja: Institute of Metallurgy and Materials Science, Kraków
Autorzy (7)
- Wójcik Anna
- Maziarz Wojciech
- Szczerba Maciej Jakub
- AGHSikora Marcin
- AGHŻywczak Antoni
- Hawełek Łukasz
- Cesari Eduard
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 119027 |
|---|---|
| Data dodania do BaDAP | 2019-01-07 |
| Tekst źródłowy | URL |
| DOI | 10.1002/pssa.201800358 |
| Rok publikacji | 2018 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | Physica Status Solidi, A, Applications and Materials Science |
Abstract
The effect of Cu substitution for Ni on the structural and magnetocaloric properties in Ni44-xCuxCo6Mn39Sn11 (x = 0-4 at.%) bulk Heusler alloys is studied. It is reported that Cu addition stabilizes austenite phase. Generally, martensitic transformation temperature decreases with an increase of Cu concentration up to 4 at.%. The addition of 1 and 2 at.% of Cu allows to shift the temperature of martensitic transformation close to room temperature, while the strong inverse magnetocaloric effect is observed in alloys containing 0-3 at.% of Cu. The value of magnetic entropy at low magnetic field of 15 kOe evolves from 6.3 J kg(-1) K-1 for Cu0 to 9.7 J kg(-1) K-1 for Cu1, 7.1 J kg(-1) K-1 for Cu2, 8.6 J kg(-1) K-1 for Cu3, and 4.1 J kg(-1) K-1 for Cu4 alloys. The estimated value of the effective refrigerant capacity, including hysteresis loss, is equal to 74.1, 80.4, 106.5, 42.6, and 77.6 J kg(-1) for Cu0, Cu1, Cu2, Cu3, and Cu4, respectively.