The influence of grain refinement and feeding quality on damping properties of the Al-20Zn cast alloy / W. K. KRAJEWSKI, K. Faerber, P. K. KRAJEWSKI // Archives of Foundry Engineering / Polish Academy of Sciences. Commission of Foundry Engineering ; ISSN 1897-3310. — Tytuł poprz.: Archiwum Odlewnictwa. — 2018 — vol. 18 iss. 2, s. 209–214. — Bibliogr. s. 213–214, Abstr.
Autorzy (3)
- AGHKrajewski Witold K.
- Haberl-Faerber K.
- AGHKrajewski Paweł Krzysztof
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 118226 |
|---|---|
| Data dodania do BaDAP | 2018-12-13 |
| Tekst źródłowy | URL |
| DOI | 10.24425/122530 |
| Rok publikacji | 2018 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Creative Commons | |
| Czasopismo/seria | Archives of Foundry Engineering |
Abstract
The paper presents relationships between the degree of structure fineness and feeding quality of the Al-20 wt.% Zn (Al-20 Zn) alloy cast into a mould made from sand containing silica quartz as a matrix and bentonite as a binder, and its damping coefficient of the ultrasound wave at frequency of 1 MHz. The structure of the examined alloy was grain refined by the addition of the refining Al-3 wt.% Ti-0.15 wt.% C (TiCAl) master alloy. The macrostructure analysis of the initial alloy without the addition of Ti and the alloy doped with 50-100 ppm Ti as well as results of damping experiments showed that the structure of the modified alloy is significantly refined. At the same time, its damping coefficient decreases by about 20-25%; however, it still belongs to the so called high-damping alloys. Additionally, it was found that despite of using high purity metals Al and Zn (minimum 99,99% purity), differences in the damping coefficient for samples cut from upper and bottom parts of the vertically cast rolls were observed. These differences are connected with the insufficient feeding process leading to shrinkage porosity as well as gases present in metal charges which are responsible for bubbles of gas-porosity.