Phase composition of $Al_{x}FeNiCrCo$ high entropy alloys prepared by sintering and arc-melting methods / J. CIEŚLAK, J. TOBOŁA, K. BERENT, M. MARCISZKO // Journal of Alloys and Compounds ; ISSN 0925-8388. — 2018 — vol. 740, s. 264–272. — Bibliogr. s. 271–272, Abstr.
Autorzy (4)
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 111944 |
|---|---|
| Data dodania do BaDAP | 2018-02-10 |
| Tekst źródłowy | URL |
| DOI | 10.1016/j.jallcom.2017.12.333 |
| Rok publikacji | 2018 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | Journal of Alloys and Compounds |
Abstract
AlxFeNiCrCo (0≤x≤1.5) high entropy alloys (HEA) have been investigated experimentally in systematic way in order to complete the existing results as well as to testify the alternative method of HEA sample preparation based on sintering of pure metallic powders. Structural properties have been studied by X-ray and neutron diffraction measurements, which allowed to identify the crystal structures and their contributions in HEA samples. The phase compositions were determined from electron microscopic measurements (EDX, EBSD). The amounts of observed BCC/B2 and FCC phases obtained using these complementary techniques remains in good agreement. Within two detected crystallographic structures, three phases with different stoichiometries were identified and their appearance, composition and contribution in the investigated HEA were found to be dependent on Al content. Comparing overall results obtained for sintered and melted samples, it was shown that the phase composition of AlxFeNiCrCo alloys are very similiar, but the corresponding microstructures are quite different, i.e. dendritic structure is observed for melted samples while large regular grains for sintered ones.