Preparation and preliminary study of the properties of electrophoretically depositied nc-${TiO_{2}}$ coatings on 316L steel — Osadzenie elektroforetyczne powłok nc-${TiO_{2}}$ na stali 316L oraz badania ich właściwości / Piotr LEDWIG, Beata DUBIEL // Inżynieria Materiałowa ; ISSN 0208-6247. — 2016 — R. 37 nr 6, s. 300–305. — Bibliogr. s. 304. — Tekst pol.-ang.
Autorzy (2)
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 103867 |
|---|---|
| Data dodania do BaDAP | 2017-01-27 |
| DOI | 10.15199/28.2016.6.4 |
| Rok publikacji | 2016 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Czasopismo/seria | IM Inżynieria Materiałowa = Materials Engineering |
Streszczenie
Celem pracy było wytworzenie powłok nc-TiO2 na stali 316L metodą osadzania elektroforetycznego zarówno anodowego, jak i katodowego, a także zbadanie ich mikrostruktury, odporności na korozję oraz zwilżalności.
Abstract
TiO2 coatings on 316L steel were obtained by use of electrophoretic deposition (EPD) method. Potential zeta of nc-TiO2 particles in suspensions containing water and ethanol in different ratios was measured. Suspensions’ pH was stabilized by addition of acetic or citric acid and ammonia solution. Addition of citric acid in small amount decreased the zeta potential. Optimal suspensions’ parameters for cathodophoretic and anodophoretic deposition were selected based on the results of zeta potential measurements versus pH for suspensions with different water–ethanol concentration. For the chosen suspensions the rate of TiO2 deposition was measured. Coatings’ cohesion was improved by sintering or addition of biopolymer (chitosan) into suspension. The microstructure of coatings was examined by scanning electron microscopy. The roughness and thickness of the coatings were measured by optical profilometer. The corrosion resistance in Ringer’s solution was examined by use of polarization curves. The corrosion resistance of coated steel was higher than that of uncoated one. For sintered coatings the corrosion currents were lower, but the passive area was larger for not sintered ones. The contact angle of the coatings was measured using a sitting drop method and superhydrophilic properties of TiO2 coatings were confirmed. Manufactured coatings may be potentially used as self-cleaning materials. Additionally, TiO2 coatings improve corrosion resistance of steel and exhibit good bactericidal properties. These characteristics may make this sort of materials potentially useful also for medical purposes.