The study of the influence of $ZrO_2$ precursor type and the temperature of annealing on the crystallization of the tetragonal polymorph of $ZrO_2$ in zirconia-silica gels / Anna ADAMCZYK // Gels [Dokument elektroniczny]. — Czasopismo elektroniczne ; ISSN 2310-2861. — 2022 — vol. 8 iss. 11 art. no. 724, s. 1–15. — Wymagania systemowe: Adobe Reader. — Bibliogr. s. 14–15, Abstr. — Publikacja dostępna online od: 2022-11-09
Autor
Słowa kluczowe
Dane bibliometryczne
| ID BaDAP | 143918 |
|---|---|
| Data dodania do BaDAP | 2022-11-30 |
| Tekst źródłowy | URL |
| DOI | 10.3390/gels8110724 |
| Rok publikacji | 2022 |
| Typ publikacji | artykuł w czasopiśmie |
| Otwarty dostęp |  |
| Creative Commons | |
| Czasopismo/seria | Gels |
Abstract
Materials of the ZrO2-SiO2 system were obtained by the sol-gel method applying two different types of ZrO2 precursors: zirconium (IV) n-propoxide Zr(OC3H7)(4) and zirconium (IV) acetate Zr(OOC2H3)(4) (organic acetic acid salt) while commonly used tetraethoxysilane TEOS was selected as SiO2 introducing one. ZrO2 concentration in synthesized samples varied from 20% to 50% (mol.). After drying for 28 days, all gels were annealed at 500 degrees C, 1000 degrees C, and 1200 degrees C in air. FTIR spectroscopy together with XRD diffraction was selected as the two main structure research methods. SEM microscopy was applied to analyze the local chemical compositions of samples and to observe the morphology of gels' surfaces. The analysis of FTIR spectra and XRD diffraction patterns allowed us to recognize different ZrO2 polymorphs which appeared in the samples depending strongly as well on ZrO2 precursor type as on the temperature of annealing. Samples synthesized by using the zirconium (IV) n-propoxide contained both cubic and tetragonal zirconia phases in general but showed the tendency of the increasing t-ZrO2 content in gels richer in ZrO2 and heated up to 1200 degrees C. However, in materials obtained applying zirconium (IV) acetate, the first detected at 500 degrees C phase was t-ZrO2 which was then conversing to m-ZrO2 form with the increasing temperature in case of samples rich in ZrO2. Meanwhile, t-ZrO2 was the predominant phase in samples of the lower content of ZrO2 but annealed at higher temperatures. By the analysis of changes in band profiles and positions, one can draw conclusions that the structure of studied samples is mostly built up of an amorphous silica matrix, in which different types of zirconia polymorphs create their own crystal lattice. The presence of the particular polymorph depends strongly on the type of zirconia precursor and the temperature of annealing.